Lightweight Insulating Fire Brick , White Mullite Insulating Brick 230 * 114 * 65mm

Yixing City Kam Tai Refractories Co.,ltd
Trust Seal
Verified Supplier
Credit Check
Supplier Assessment
Yixing City Kam Tai Refractories Co.,ltd
Province/State: Jiangsu
Country/Region: China
Tel: 86-510-87997800-803
Contact Person:
Mr Bruce

Lightweight Insulating Fire Brick , White Mullite Insulating Brick 230 * 114 * 65mm

Brand Name : KAMTAI
Model Number : KTRKF7
Certification : ISO
Place of Origin : CHINA
MOQ : 3000 PCS
Price : Negotiable
Payment Terms : T/T, L/C, Western Union, MoneyGram,Paypal
Supply Ability : 50000PCS/MONTH
Delivery Time : 25 DAYS AFTER PAYMENT
Packaging Details : PLYWOOD BOX AND PALLET
Color : White
Using temperature : 1300-1600℃
Density : 0.6-1.2g/cm3
Al2O3 ≥% : 40
Fe2O3 ≥% : 0.7
Size : 230*114*65/75mm
Contact Now

High heat refractory kiln furniture Mullite lightweight insulation brick 230 * 114 * 65mm


1. Description

Mullite (3 2 sio2, al2o3) phase of high aluminum refractory material. General alumina content is between 65% ~ 75%. Mineral composition in addition to the mullite, contain the alumina lower also contains a small amount of glass phase and cristobalite; Containing alumina high contains a small amount of corundum.High refractoriness, can reach more than 1790 ℃. The rul start temperature of 1600 ~ 1700 ℃. Room temperature compressive strength of 70 ~ 260 mpa. Good thermal shock resistance. A sintered mullite bricks and two fused mullite brick.

Sintered mullite brick with high bauxite clinker as the main raw material, add a small amount of clay or raw bauxite as binder, forming, sintering and made. Fused mullite brick with high alumina, alumina industry and refractory clay as raw material, adding charcoal or coke fine as a reducing agent, reduction fused method is used to manufacture after forming.


2. Specification

Item13001450155016500.5
ASTM C155-84 Classification23262830
ISO 2245 Classification125-0.5-L140-0.8-L150-0.9-L160-1.0-L
Classification Temperature1260143015401650

g/cm³

Bulk Density

ASTM C-134-84

0.60.80.91.00.55

Cold Crushing Strength

ASTM C-93-847(MPa)


1.53.03.54.01.2
Thermal Expansion At 1100℃0.50.50.580.6≤1.5(900℃)
Thermal shock Resistance Cycles30303030
Thermal Conductivity ASTM C182-88W/m.k4000.140.270.320.41≤0.15
6000.160.290.340.43
8000.180.310.360.44
10000.200.330.380.45
12000.350.410.47
Al2O3 %37526773
Fe2O3 %1.31.00.80.6

3. Features

Low Thermal Conductivity

It has good insulation effect and can thin the thickness of furnace wall.

Low thermal capacity

Less heat storage, it has good usage effect in intermittent furnace.

Good thermal shock resistance and high temperature strength

It can prolong the service life of kilns and prevent dirty slag to drop down.

Precise dimension

It can keep uniform gaps between each brick, speed up the building, guarantee the integrated high strength of the masonry.

Low impurity

Lower iron and alkali content, it has high resistance to reduce atmosphere corrosion at high temperature.

4. Application

It is mainly used for hot blast stove top, blast furnace and furnace bottom, the regenerator of glass furnace, ceramic sintering kiln, petroleum cracking system corner lining, etc. Also widely used in hot blast stove, metal furnace, ceramic tunnel kilnelectrical porcelain shuttle kiln, etc., has a broad market prospect.



Product Tags:

alumina ceramic disc

      

high alumina kiln shelves

      
China Customized Inflatable Bumper Ball Game Bubble Adult Grass CE supplier

Lightweight Insulating Fire Brick , White Mullite Insulating Brick 230 * 114 * 65mm Images

Inquiry Cart 0
Send your message to this supplier
 
From:
Enter your email please.
To: Yixing City Kam Tai Refractories Co.,ltd
Subject:
Message:
Characters Remaining: (0/3000)
 

Home| Products| Suppliers| Quality Suppliers| Site Map |About Us |Contact Us |Help |关于我们 |联系我们

Copyright © 2009 - 2018 bjjsgy.com. All rights reserved.